Thutong ena, re ile ra batlisisa li-Cu/Ni nanoparticles tse entsoeng mehloling ea microcarbon nakong ea tšebelisano-'moho ke RF sputtering le RF-PECVD, hammoho le sebaka sa sebaka sa plasmon resonance bakeng sa ho lemoha khase ea CO ho sebelisa Cu/Ni nanoparticles.Morphology ea likaroloana.Surface morphology e ile ea ithutoa ka ho sekaseka li-micrograph tsa 3D atomic force ho sebelisa ts'ebetso ea litšoantšo le mekhoa ea tlhahlobo ea fractal/multifractal.Tlhahlobo ea lipalo-palo e entsoe ho sebelisoa software ea MountainsMap® Premium e nang le tlhahlobo ea mekhoa e 'meli ea phapang (ANOVA) le tlhahlobo e nyane ea phapang e kholo.Li-nanostructures tsa sefahleho li na le kabo e khethehileng ea lehae le ea lefats'e.Liteko le tse etsisitsoeng tsa Rutherford tsa backscattering spectra li netefalitse boleng ba nanoparticles.Mehlala e sa tsoa lokisoa e ile ea pepesetsoa chimney ea carbon dioxide mme ts'ebeliso ea eona e le sensor ea khase e ile ea fuputsoa ho sebelisoa mokhoa oa sebaka sa sebaka sa plasmon resonance.Ho eketsoa ha lesela la nickel ka holim'a lera la koporo ho ile ha bontša liphello tse thahasellisang ka bobeli mabapi le morpholoji le ho lemoha khase.Motsoako oa tlhahlobo e tsoetseng pele ea stereo ea topography ea filimi e tšesaane e nang le " Rutherford backscattering spectroscopy le spectroscopic analysis e ikhethile lebaleng lena.
Tšilafalo ea moea e potlakileng lilemong tse mashome a seng makae tse fetileng, haholo-holo ka lebaka la tsoelo-pele e potlakileng ea indasteri, e susumelitse bafuputsi ho ithuta ho eketsehileng ka bohlokoa ba ho lemoha likhase.Metal nanoparticles (NPs) e bontšitsoe e le lisebelisoa tse tšepisang bakeng sa li-sensors tsa khase1,2,3,4 esita le ha li bapisoa le lifilimi tse tšesaane tsa tšepe tse khonang ho etsa sebaka sa plasmon resonance (LSPR), e leng ntho e lumellanang le motlakase o matla le o fokolang ka matla. masimo5,6,7,8.Joalo ka tšepe ea phetoho e sa tureng, e chefo e tlase ebile e sebetsa ka mokhoa o fapaneng, koporo e nkuoa e le ntho ea bohlokoa ke bo-ramahlale le indasteri, haholo baetsi ba lisensara9.Ka lehlakoreng le leng, li-catalyst tsa tšepe tsa nickel transition li sebetsa hantle ho feta li-catalysts tse ling10.Tšebeliso e tsebahalang ea Cu / Ni ho nanoscale e etsa hore e be ea bohlokoa le ho feta, haholo-holo hobane thepa ea bona ea sebopeho ha e fetohe ka mor'a fusion11,12.
Le hoja li-nanoparticles tsa tšepe le li-interface tsa tsona le sebaka sa dielectric li bonts'a liphetoho tse kholo ho li-plasmon resonances tsa sebakeng seo, li 'nile tsa sebelisoa e le litšiea tsa ho haha bakeng sa ho lemoha khase13.Ha matla a ho monya a fetoha, sena se bolela hore lintlha tse tharo tsa "resonant wavelength" le / kapa matla a tlhōrō ea ho monya le / kapa FWHM li ka fetoha ka 1, 2, 3, 4. Likarolong tse nang le nanostructured, tse amanang ka ho toba le boholo ba likaroloana, sebaka sa libaka. plasmon resonance ho nanoparticles, eseng lifiliming tse tšesaane, ke ntho e sebetsang bakeng sa ho tsebahatsa ho monya ha molek'hule14, joalo ka ha ho boletsoe ke Ruiz et al.e bontšitse kamano pakeng tsa likaroloana tse ntle le bokhoni ba ho lemoha15.
Mabapi le ho lemoha ha optical ea CO khase, lisebelisoa tse ling tse kopantsoeng tse kang AuCo3O416, Au-CuO17 le Au-YSZ18 li tlalehiloe libukeng.Re ka nahana ka khauta e le tšepe e ntle e kopantsoeng le li-oxide tsa tšepe ho bona limolek'hule tsa khase tse kentsoeng ka lik'hemik'hale holim'a motsoako, empa bothata bo ka sehloohong ba li-sensor ke tsela eo li itšoarang ka eona mochesong oa kamore, e leng se etsang hore li se ke tsa fumaneha.
Lilemong tse mashome a seng makae tse fetileng, atomic force microscopy (AFM) e 'nile ea sebelisoa e le mokhoa o tsoetseng pele oa ho tšoaea micromorphology ea mahlakore a mararo boemong bo phahameng ba nanoscale19,20,21,22.Ho phaella moo, stereo, fractal/multifractal analysis23,24,25,26, power spectral density (PSD)27 le Minkowski28 functionals ke lisebelisoa tsa morao-rao bakeng sa ho khetholla boemo ba holimo ba lifilimi tse tšesaane.
Thutong ena, ho ipapisitsoe le ho monya ha plasmon resonance (LSPR) sebakeng sa lehae, mesaletsa ea acetylene (C2H2) Cu/Ni NP e kentsoe mochesong oa kamore hore e sebelisoe joalo ka lisensara tsa khase ea CO.Rutherford backscatter spectroscopy (RBS) e ile ea sebelisoa ho sekaseka sebopeho le morphology ho tsoa litšoantšong tsa AFM, 'me limmapa tsa topographic tsa 3D li ile tsa sebetsoa ho sebelisoa software ea MountainsMap® Premium ho ithuta holim'a isotropy le likarolo tsohle tsa tlatsetso tsa micromorphological tsa top microtextures.Ka lehlakoreng le leng, liphetho tse ncha tsa mahlale li bonts'itsoe tse ka sebelisoang lits'ebetsong tsa indasteri mme li na le thahasello e kholo lits'ebetsong tsa tlhahlobo ea khase ea lik'hemik'hale (CO).Lingoliloeng li tlaleha ka lekhetlo la pele ho qaptjoa, ho khetholla le ho sebelisoa ha nanoparticle ena.
Filimi e tšesaane ea Cu/Ni nanoparticles e lokiselitsoe ke RF sputtering le RF-PECVD co-deposition ka phepelo ea matla ea 13.56 MHz.Mokhoa o thehiloe holim'a mochini o nang le li-electrode tse peli tsa lisebelisoa le boholo bo fapaneng.E nyenyane ke tšepe e le electrode e matlafalitsoeng, 'me e kholoanyane e thehiloe ka kamoreng ea tšepe e sa hloekang e le sebaka sa 5 cm ho tloha ho e mong.Beha substrate ea SiO 2 le sepheo sa Cu ka kamoreng, ebe u tlosa kamoreng ho 103 N / m 2 e le khatello ea motheo mocheso oa mocheso, kenya khase ea acetylene ka kamoreng, ebe u hatella khatello ea tikoloho.Ho na le mabaka a mabeli a ka sehloohong a ho sebelisa khase ea acetylene mohatong ona: ea pele, e sebetsa e le khase e tsamaisang tlhahiso ea plasma, 'me ea bobeli, bakeng sa ho lokisa li-nanoparticles ka bongata ba carbon.Ts'ebetso ea deposition e ile ea etsoa bakeng sa metsotso e 30 ka khatello ea pele ea khase le matla a RF a 3.5 N/m2 le 80 W, ka ho latellana.Ebe u roba sekheo 'me u fetole sepheo ho Ni.Ts'ebetso ea deposition e ile ea phetoa ka khatello ea pele ea khase le matla a RF a 2.5 N/m2 le 150 W, ka ho latellana.Qetellong, li-nanoparticles tsa koporo le tsa nickel tse kentsoeng moeeng oa acetylene li theha nanostructures ea koporo / nickel.Sheba Lethathamo la 1 bakeng sa mohlala oa ho lokisoa le li-identifiers.
Litšoantšo tsa 3D tsa lisampole tse sa tsoa lokisoa li ile tsa tlalehoa sebakeng sa 1 μm × 1 μm lisekoere tsa lisekoere ho sebelisa nanometer multimode atomic force microscope (Digital Instruments, Santa Barbara, CA) ka mokhoa o sa kopanang le lebelo la 10-20 μm / min. .Ka.Software ea MountainsMap® Premium e sebelisitsoe ho sebetsana le 'mapa oa 3D AFM oa boemo ba leholimo.Ho ea ka ISO 25178-2: 2012 29,30,31, likarolo tse 'maloa tsa morphological li ngotsoe le ho buisanoa, bophahamo, mokokotlo, molumo, sebopeho, mosebetsi, sebaka le motsoako li hlalosoa.
Botenya le sebopeho sa lisampole tse sa tsoa lokisoa li ile tsa hakanngoa ka tatellano ea MeV e sebelisang matla a phahameng a Rutherford a backscattering spectroscopy (RBS).Tabeng ea ho hlahloba khase, LSPR spectroscopy e ile ea sebelisoa ho sebelisoa UV-Vis spectrometer sebakeng sa wavelength ho tloha 350 ho ea ho 850 nm, ha sampuli ea moemeli e ne e le ka har'a cuvette ea tšepe e sa hloekang e nang le bophara ba 5.2 cm le bolelele ba 13.8 cm. ka bohloeki ba 99.9% CO khase ea phallo ea khase (ho ea ka Arian Gas Co. IRSQ standard, 1.6 ho 16 l / h bakeng sa metsotsoana ea 180 le metsotsoana ea 600).Mohato ona o entsoe ka mocheso oa kamore, mongobo o ka hare oa 19% le hood ea mouoane.
Rutherford backscattering spectroscopy e le mokhoa oa ho hasanya ion o tla sebelisoa ho sekaseka sebopeho sa lifilimi tse tšesaane.Mokhoa ona o ikhethang o lumella quantification ntle le tšebeliso ea litekanyetso tsa litšupiso.Tlhahlobo ea RBS e lekanya matla a phahameng (He2+ ion, ke hore likaroloana tsa alpha) ka tatellano ea MeV ho sampole le li-ion tsa He2+ tse hasaneng ka lehlakoreng le itseng.Khoutu ea SIMNRA e thusa ho etsa mohlala oa mela e otlolohileng le li-curve, 'me ngollano ea eona ho sebopeho sa liteko sa RBS e bonts'a boleng ba lisampole tse lokisitsoeng.Sekhahla sa RBS sa sampuli ea Cu / Ni NP se bontšoa ho Setšoantšo sa 1, moo mohala o mofubelu e leng teko ea liteko tsa RBS, 'me mohala o moputsoa ke papiso ea lenaneo la SIMNRA, ho ka bonoa hore mela e 'meli ea spectral e ntle. tumellano.Lebala la ketsahalo le nang le matla a 1985 keV le ile la sebelisoa ho tsebahatsa likarolo tsa sampole.Botenya ba lera e ka holimo ke hoo e ka bang 40 1E15Atom / cm2 e nang le 86% Ni, 0,10% O2, 0,02% C le 0,02% Fe.Fe e amahanngoa le litšila sebakeng sa Ni target nakong ea ho fafatsa.Litlhōrō tsa Cu le Ni tse ka tlaase li bonahala ho 1500 keV, ka ho latellana, le litlhōrō tsa C le O2 ho 426 keV le 582 keV, ka ho latellana.Mehato ea Na, Si, le Fe ke 870 keV, 983 keV, 1340 keV, le 1823 keV, ka ho latellana.
Litšoantšo tsa AFM tsa Square 3D tsa sebopeho sa filimi tsa Cu le Cu/Ni NP li bonts'oa ho Feiga.2. Ho phaella moo, setšoantšo sa 2D se hlahisitsoeng setšoantšong se seng le se seng se bontša hore li-NP tse hlokometsoeng holim'a filimi li kopana ho ba libopeho tse chitja, 'me morpholoji ena e tšoana le e hlalositsoeng ke Godselahi le Armand32 le Armand et al.33.Leha ho le joalo, li-NP tsa rona tsa Cu li ne li sa kopane, 'me sampuli e nang le Cu feela e bontšitse sebaka se boreleli haholo se nang le litlhōrō tse ntle ho feta tse thata (setšoantšo sa 2a).Ho e-na le hoo, litlhōrō tse bulehileng ka lisampole tsa CuNi15 le CuNi20 li na le sebōpeho se hlakileng sa spherical le matla a phahameng, joalokaha ho bontšoa ke tekanyo ea bophahamo ho Fig. 2a le b.Phetoho e bonahalang ea morphology ea filimi e bontša hore bokaholimo bo na le likarolo tse fapaneng tsa sebaka sa topographical, tse angoang ke nako ea ho beha nickel.
Litšoantšo tsa AFM tsa Cu (a), CuNi15 (b), le CuNi20 (c) lifilimi tse tšesaane.Limmapa tse nepahetseng tsa 2D, likabelo tse phahameng le li-curve tsa Abbott Firestone li kentsoe setšoantšong ka seng.
Karolelano ea boholo ba lijo-thollo tsa nanoparticles e ne e hakanngoa ho tloha histogram ea kabo ea bophara e fumanoeng ka ho lekanya li-nanoparticles tse 100 ho sebelisoa ho lekana ha Gaussian joalokaha ho bontšitsoe ho FIG.Ho ka bonoa hore Cu le CuNi15 li na le boholo bo lekanang ba lijo-thollo (27.7 le 28.8 nm), ha CuNi20 e na le lijo-thollo tse nyenyane (23.2 nm), tse haufi le boleng bo tlalehiloeng ke Godselahi et al.34 (hoo e ka bang 24 nm).Lits'ebetsong tsa bimetallic, litlhōrō tsa sebaka sa sebaka sa plasmon resonance li ka fetoha ka phetoho ea boholo ba lijo-thollo35.Tabeng ena, re ka fihlela qeto ea hore nako e telele ea ho beha Ni e ama thepa ea plasmonic ea holim'a Cu / Ni lifilimi tse tšesaane tsa tsamaiso ea rona.
Kabo ea boholo ba karolo ea (a) Cu, (b) CuNi15, le (c) CuNi20 lifilimi tse tšesaane tse fumanoeng ho tsoa ho AFM topography.
Bulk morphology e boetse e phetha karolo ea bohlokoa tlhophisong ea sebaka sa sebopeho sa boemo ba leholimo lifiliming tse tšesaane.Letlapa la 2 le thathamisa liparamente tsa boemo ba leholimo tse thehiloeng ho bophahamo tse amanang le 'mapa oa AFM, o ka hlalosoang ke boleng ba nako ea bokhopo bo boholo (Sa), skewness (Ssk), le kurtosis (Sku).Litekanyetso tsa Sa ke 1.12 (Cu), 3.17 (CuNi15) le 5.34 nm (CuNi20), ka ho latellana, ho tiisa hore lifilimi li fetoha tse thata ka nako e ntseng e eketseha ea Ni deposition.Litekanyetso tsena li bapisoa le tse tlalehiloeng pele ke Arman et al.33 (1-4 nm), Godselahi et al.34 (1-1.05 nm) le Zelu et al.36 (1.91-6.32 nm), moo e tšoanang le eona. sputtering e ne e etsoa ho sebelisoa mekhoa ena ho kenya lifilimi tsa Cu/Ni NPs.Leha ho le joalo, Ghosh et al.37 ba kentse li-multilayer tsa Cu / Ni ka electrodeposition mme ba tlaleha litekanyetso tse phahameng tsa ho ba boima, ho bonahala eka ke 13.8 ho 36 nm.Hoa lokela ho hlokomeloa hore liphapang tsa kinetics ea sebopeho sa bokaholimo ka mekhoa e fapaneng ea deposition li ka lebisa ho thehoeng ha libaka tse nang le mekhoa e fapaneng ea sebaka.Leha ho le joalo, ho ka bonoa hore mokhoa oa RF-PECVD o sebetsa hantle bakeng sa ho fumana lifilimi tsa Cu/Ni NPs tse nang le boima bo sa feteng 6.32 nm.
Ha e le profil ea bophahamo, linako tse phahameng tsa lipalo-palo Ssk le Sku li amana le asymmetry le ho tloaeleha ha kabo ea bophahamo, ka ho latellana.Litekanyetso tsohle tsa Ssk li ntle (Ssk> 0), e bontšang mohatla o molelele o nepahetseng38, o ka tiisoang ke morero oa kabo ea bophahamo ho inset 2. Ho phaella moo, litlaleho tsohle tsa bophahamo li ne li laoloa ke tlhōrō e bohale 39 (Sku> 3) , e bonts'ang hore curve Kabo ea bophahamo ha e bataletse ho feta mokokotlo oa tšepe oa Gaussian.Mohala o mofubelu sebakeng sa kabo ea bophahamo ke lekhalo la Abbott-Firestone 40, mokhoa o loketseng oa lipalo-palo oa ho lekola kabo e tloaelehileng ea data.Mohala ona o fumanoa ho tsoa kakaretsong ea kakaretso ea histogram ea bophahamo, moo tlhōrō e phahameng ka ho fetisisa le sekoti se tebileng ka ho fetisisa li amanang le bonyane ba tsona (0%) le boholo ba (100%).Li-curve tsena tsa Abbott-Firestone li na le sebopeho se boreleli sa S holim'a y-axis 'me maemong' ohle li bonts'a keketseho e tsoelang pele ea peresente ea thepa e tšetsoeng sebakeng se koahetsoeng, ho qala ho tloha tlhorong e thata le e matla ka ho fetisisa.Sena se tiisa sebopeho sa sebaka sa bokaholimo, se angoang haholo ke nako ea ho beha nickel.
Letlapa la 3 le thathamisa liparamente tse ikhethileng tsa sebopeho sa ISO tse amanang le bokaholimo bo bong le bo bong bo fumanoang litšoantšong tsa AFM.Hoa tsebahala hore karo-karolelano ea sebaka le thepa (Smr) le sebaka sa counter to material ratio (Smc) ke mekhahlelo ea tšebetso ea bokaholimo29.Ka mohlala, liphetho tsa rona li bontša hore sebaka se ka holimo ho sefofane se bohareng se holimo ka ho feletseng lifiliming tsohle (Smr = 100%).Leha ho le joalo, boleng ba Smr bo fumanoa ho tsoa bophahamong bo fapaneng ba sebaka se behiloeng sa sebaka sa terrain41, kaha parameter Smc e tsejoa.Boitšoaro ba Smc bo hlalosoa ke ho eketseha ha bohale ho tloha Cu → CuNi20, moo ho ka bonoang hore boleng bo phahameng ka ho fetisisa bo fumanoeng bakeng sa CuNi20 bo fana ka Smc ~ 13 nm, ha boleng ba Cu bo ka bang 8 nm.
Mekhahlelo ea ho kopanya RMS gradient (Sdq) le karo-karolelano ea sebaka se ntlafalitsoeng (Sdr) ke liparamente tse amanang le ho hlaka ha sebopeho le ho rarahana.Ho tloha ho Cu → CuNi20, litekanyetso tsa Sdq li tloha ho 7 ho isa ho 21, e leng se bontšang hore ho se tloaelehe ha boemo ba leholimo lifiliming ho eketseha ha Ni layer e behoa metsotso e 20.Ho lokela ho hlokomeloa hore bokaholimo ba CuNi20 ha bo bataletse joalo ka Cu.Ho phaella moo, ho ile ha fumanoa hore boleng ba parameter Sdr, e amanang le ho rarahana ha microtexture ea holim'a metsi, e eketseha ho tloha Cu → CuNi20.Ho ea ka phuputso ea Kamble et al.42, ho rarahana ha sefahleho sa microtexture ho eketseha ka Sdr e ntseng e eketseha, e bontšang hore CuNi20 (Sdr = 945%) e na le microstructure e rarahaneng ea holim'a metsi ha e bapisoa le lifilimi tsa Cu (Sdr = 229%)..Ha e le hantle, phetoho ea ho rarahana ha microscopic ea sebopeho e phetha karolo ea bohlokoa kabong le sebōpehong sa litlhōrō tse mahlahahlaha, tse ka bonoang ho tloha ho likarolo tse khethollang tsa peak density (Spd) le arithmetic mean peak curvature (Spc).Tabeng ena, Spd e eketseha ho tloha Cu → CuNi20, e leng se bontšang hore litlhōrō li hlophisitsoe ka mokhoa o tsitsitseng ka ho eketseha ha botenya ba Ni layer.Ho phaella moo, Spc e boetse e eketseha ho tloha Cu→ CuNi20, e bontšang hore sebopeho sa tlhōrō ea holim'a sampuli ea Cu se pota-potiloe haholoanyane (Spc = 612), ha CuNi20 e le bohale (Spc = 925).
Boemo bo bobe ba filimi e 'ngoe le e' ngoe bo boetse bo bonts'a mekhoa e ikhethileng ea sebaka libakeng tse phahameng, tse bohareng le tse holim'a metsi.Bophahamo ba mantlha (Sk), tlhoro e fokotsehang (Spk) (kaholimo ho konokono), le sekoti (Svk) (ka tlase ho mantlha) 31,43 ke liparamente tse lekantsoeng ka tsela e lekanang le sefofane30 le ho eketseha ho tloha Cu → CuNi20 ka lebaka la bokahodimo ba bokahodimo Keketseho e kgolo .Ka mokhoa o ts'oanang, lisebelisoa tsa tlhoro (Vmp), lisebelisoa tsa mantlha (Vmc), trough void (Vvv), le core void volume (Vvc)31 li bonts'a mokhoa o ts'oanang le ha litekanyetso tsohle li eketseha ho tloha Cu → CuNi20.Boitšoaro bona bo bontša hore sebaka sa CuNi20 se ka tšoara metsi a mangata ho feta lisampole tse ling, tse ntle, tse fanang ka maikutlo a hore sebaka sena se bonolo ho smear44.Ka hona, hoa lokela ho hlokomeloa hore ha botenya ba lera la nickel le eketseha ho tloha CuNi15 → CuNi20, liphetoho tsa boemo ba topographic li lag ka mor'a liphetoho tsa litekanyetso tse phahameng tsa morphological, tse amang holim'a microtexture le mokhoa oa sebaka sa filimi.
Tekolo ea boleng ba sebopeho sa microscopic ea bokaholimo ba filimi e fumanoe ka ho aha 'mapa oa boemo ba leholimo oa AFM ho sebelisoa software ea khoebo ea MountainsMap45.Phetolelo e bontšoa ho Setšoantšo sa 4, se bontšang groove ea moemeli le polar plot mabapi le bokaholimo.Lethathamo la 4 le thathamisa sebaka le likhetho tsa sebaka.Litšoantšo tsa li-grooves li bontša hore sampuli e laoloa ke tsamaiso e tšoanang ea likanale tse nang le homogeneity e boletsoeng ea li-grooves.Leha ho le joalo, litekanyo tsa botebo bo boholo ba groove (MDF) le botebo bo boholo ba groove (MDEF) li eketseha ho tloha Cu ho ea CuNi20, e leng se tiisang se hlokometsoeng nakong e fetileng mabapi le matla a lubricity a CuNi20.Re lokela ho hlokomela hore Cu (sa feiga. 4a) le CuNi15 (sa feiga. 4b) disampole na hoo e ka bang e tšoanang 'mala sekala, e leng se bontšang hore microtexture ea Cu filimi holim'a se ke ua etsa liphetoho tse khōlō ka mor'a hore filimi Ni e ne e behoa bakeng sa 15 min.Ka lehlakoreng le leng, sampuli ea CuNi20 (setšoantšo sa 4c) e bonts'a masoba a nang le sekala sa mebala e fapaneng, e amanang le litekanyetso tsa eona tse phahameng tsa MDF le MDEF.
Li-grooves le isotropy ea holim'a li-microtextures tsa Cu (a), CuNi15 (b), le CuNi20 (c) lifilimi.
Setšoantšo sa polar ka feiga.4 e boetse e bontša hore microtexture e ka holimo e fapane.Hoa hlokomeleha hore ho behoa ha Ni layer ho fetola haholo mokhoa oa sebaka.The microtextural isotropy e baloang ea disampole e ne e le 48% (Cu), 80% (CuNi15), le 81% (CuNi20).Ho ka bonoa hore deposition ea Ni lera kenya letsoho hore ho thehoe ho feta isotropic microtexture, ha e le 'ngoe lera Cu filimi na le ho feta anisotropic holim microtexture.Ho feta moo, maqhubu a maholo a sebaka sa CuNi15 le CuNi20 a tlase ka lebaka la bolelele ba bona bo boholo ba autocorrelation (Sal) 44 bapisoa le lisampole tsa Cu.Sena se boetse se kopantsoe le mokhoa o tšoanang oa lijo-thollo o bontšitsoeng ke mehlala ena (Std = 2.5 ° le Std = 3.5 °), ha boleng bo boholo haholo bo tlalehiloe bakeng sa sampuli ea Cu (Std = 121 °).Ho ipapisitsoe le liphetho tsena, lifilimi tsohle li bonts'a liphapang tsa sebaka se selelele ka lebaka la sebopeho se fapaneng, boemo ba boemo ba leholimo le bokhopo.Ka hona, liphetho tsena li bonts'a hore nako ea deposition ea Ni layer e phetha karolo ea bohlokoa ho thehoeng ha libaka tsa CuNi bimetallic sputtered.
Ho ithuta ka boits'oaro ba LSPR ba Cu/Ni NPs moeeng ka mocheso oa kamore le ka likhase tse fapaneng tsa CO, ho ile ha sebelisoa mahlaseli a UV-Vis sebakeng sa leqhubu la 350-800 nm, joalo ka ha ho bonts'itsoe ho Setšoantšo sa 5 bakeng sa CuNi15 le CuNi20.Ka ho hlahisa likhahla tse fapaneng tsa phallo ea khase ea CO, tlhōrō e sebetsang ea LSPR CuNi15 e tla ba e pharaletseng, ho monya ho tla ba matla, 'me tlhōrō e tla fetoha (redshift) ho ea ho maqhubu a phahameng, ho tloha ho 597.5 nm ho ea ho 16 L / h 606.0 nm.CO e phalla ka metsotsoana ea 180, 606.5 nm, CO e phalla 16 l / h bakeng sa metsotsoana e 600.Ka lehlakoreng le leng, CuNi20 e bonts'a boitšoaro bo fapaneng, kahoo ho eketseha ha phallo ea khase ea CO ho fella ka ho fokotseha ha LSPR peak wavelength position (blueshift) ho tloha 600.0 nm moeeng oa ho phalla ho 589.5 nm ho 16 l / h CO phallo bakeng sa 180 s. .16 l / h CO e phalla ka metsotsoana ea 600 ho 589.1 nm.Joalo ka CuNi15, re ka bona tlhoro e pharalletseng le ho eketseha ha matla a ho monya bakeng sa CuNi20.Ho ka hakanngoa hore ka keketseho ea botenya ba Ni layer ka Cu, hammoho le keketseho ea boholo le palo ea CuNi20 nanoparticles ho e-na le likaroloana tsa CuNi15, Cu le Ni li atamelana, amplitude ea oscillations ea elektronike e eketseha. , 'me, ka lebaka leo, maqhubu a eketseha.e bolelang: bolelele ba maqhubu bo fokotseha, ho etsahala phetoho e putsoa.